UTF-100
UTF-100 is a high-temperature release film in thickness 25 µm made of modified PET with excellent separating properties and unique high temperature stability. Laminates pressed with UTF-100 can be further processed immediately without an additional after-treatment and remain solderable. UTF-100 release film contains no silicone and the press plates remain clean. UTF-100 is inexpensive and eco-friendly; no toxic fission products are produced during combustion. The film is also available in thickness 38 µm (UTF-150).
Delivery form: rolls with 1067 m and cuttings
Thickness: 25 µm (UTF-100); 38 µm (UTF-150)
Roll width: 305 – 1360 mm
Max. laminating temperature: about 210°C, depending on pressing conditions
Further information see technical datasheet:
UTF-100_TDS(3) | |
05.07.2017 07:30:42 125.95 KB 1,853 | Download |
UTF-150_TDS(2) | |
05.07.2017 07:31:30 125.86 KB 1,706 | Download |
VTF-400 RW
VTF-400 RW is a universal release film for pressing flexibel and rigid multilayers. The film has no surface coating. Nevertheless the product offers good release properties against many materials and resin systems.
Delivery form: rolls and cuttings
Thickness: 40 µm
Roll width: 610 mm; 1285 mm (maximum)
Max. laminating temperature: 190 °C
TTF-25
TTF-25 release film is based on PTFE and therefore chemically inert and boasts a very high thermal stability. Making it particularly well-suited for laminating processes with very high pressing temperatures or application on surfaces that show contact reactions and react sensitively to polymer residues.
Delivery form: rolls and cuttings
Thickness: 25 µm; also available in further thicknesses (50 ... 500 µm).
Roll width: 460, 610, 660 mm
Max. laminating temperature: 260°C
Further information see technical datasheet:
TTF-25_TDS(1) | |
05.07.2017 07:35:40 127.43 KB 1,582 | Download |
ATF-50
The release film ATF-50 is made of a special aluminium alloy and prevents the pressing-in of release film or pressure compensation material in the existing drill holes of the product to be pressed during lamination of coverlays on flexible and rigid-flexible PCBs. ATF-50 also prevents the "orange peel effect" on coverlays and is useful in suppressing image transfer. Positioning: between release film and press pad or pressure compensation foil.
Delivery form: rolls of 250 kg and cuttings (drilled or stamped on request)
Thickness: 50 µm
Roll width: 650 mm
Further information see technical datasheet:
ATF-50_TDS(1) | |
05.07.2017 09:53:59 204.02 KB 1,543 | Download |